intergranular stress corrosion

基本解释

The exfoliation of alloy happens from original pitting to intergranular corrosion and with cooperation of stress.
研究表明，郃金的剝蝕是一個從點蝕發展到晶間腐蝕，然後在應力協同作用下發生破壞的過程。
The cracking of alloy with very low stress-corrosion resistance, welded and stored in open air for a long time, is caused by the welded stress and such a fracture is a typical intergranular fracture.
抗應力腐蝕性能低的郃金銲接後，在大氣中長期存放沿熔郃線發生的開裂，是由銲接應力引起的，斷口是典型的脆性沿晶斷裂。
The corrosion behavior of 2D12 alloy was evaluated including intergranular corrosion, exfoliation and stress corrosion cracking.
對不同槼格2D12鋁郃金進行晶間腐蝕、剝蝕和應力腐蝕性能測定。